Muki EPS
Product Description
This is a two component chemically curing epoxy coating. It is a shop primer designed for high welding and cutting speed, giving reduced weld porosity and back burning. It is fast drying making it suitable for stacking shortly after application. Can be used as temporary primer in a new construction phase, as holding primer or as primer in a complete coating system in atmospheric and immersed environments. Suitable for properly prepared carbon steel substrates and recommended to be applied in an automated shop priming line in lower film thicknesses or applied by airless spray when used as holding primer. Compatible with advanced welding
technologies including MIG, MAG and G-FCAW when applied in low film thickness.
Product data
Film thickness per coat
Drying and curing time
Product data
| Property | Test/Standard | Description |
|---|---|---|
| Solids by volume | ISO 3233 | 25 ± 2 % |
| Gloss level (GU 60 °) | ISO 2813 | semi gloss (0 – 35) |
Film thickness per coat
- Typical recommended specification range
| STANDARD GRADE | |
|---|---|
| Dry film thickness | 15 – 50 μm |
| Wet film thickness | 60 – 200 μm |
| Theoretical spreading rate | 16.7 – 5 m²/l |
Drying and curing time
| Substrate temperature | 5 °C | 10 °C | 23 °C | 40 °C |
|---|---|---|---|---|
| Surface (touch) dry | 15 min | 10 min | 1 min | 20 sec |
| Walk-on-dry | 20 min | 15 min | 4 min | 1 min |