Jotatemp 1000
Product Description
This is a three component titanium catalyzed inorganic ceramic copolymer based coating. It complies to the generic type Inert Multi Polymeric Matrix Coating. Designed as a heat resistant coating, and it is resistant to low temperatures down to -196 °C and high temperatures up to 1000 °C continuously, where substrates allow. Can be used as primer or finish coat in atmospheric environments. Suitable for properly prepared carbon steel, stainless steel and ceramic substrates. It can be applied on hot substrates up to 250 °C.
The product passes the standard tests used for qualifying coatings preventing corrosion under insulation (CUI).
It will offer proper corrosion protection at ambient conditions during construction and shut-down periods.
Product data
Film thickness per coat
Drying and curing time
Product data
| Property | Test/Standard | Description |
|---|---|---|
| Solids by volume | ISO 3233 | 75 ± 2 % |
| Gloss level (GU 60 °) | ISO 2813 | matt (0-35) |
Film thickness per coat
- Typical recommended specification range
| STANDARD GRADE | |
|---|---|
| Dry film thickness | 100 – 150 μm |
| Wet film thickness | 130 – 200 μm |
| Theoretical spreading rate | 7.5 – 5 m²/l |
Drying and curing time
| Substrate temperature | 10 °C | 15 °C | 23 °C | 40 °C |
|---|---|---|---|---|
| Surface (touch) dry | 5.5 h | 3 h | 2.5 h | 1.5 h |
| Walk-on-dry | 24 h | 18 h | 6 h | 3.5 h |