Muki Z 2001
Product Description
This is a two component inorganic low zinc moisture curing zinc ethyl silicate coating. It is a shop primer designed for very high welding and cutting speed, giving reduced weld porosity and back burning. It is fast drying and has good abrasion resistance making it suitable for stacking shortly after application. Can be used as temporary primer in a new construction phase or as primer in a complete coating system in atmospheric and immersed environments. Suitable for properly prepared carbon steel substrates and recommended to be applied in an automated shop priming line. Compatible with advanced welding technologies including MIG, MAG and GFCAW.
Product data
Film thickness per coat
Drying and curing time
Product data
| Property | Test/Standard | Description |
|---|---|---|
| Solids by volume | ISO 3233 | 28 ± 2 % |
| Gloss level (GU 60 °) | ISO 2813 | semi gloss (0 – 35) |
Film thickness per coat
- Typical recommended specification range
| STANDARD GRADE | |
|---|---|
| Dry film thickness | 15 – 20 μm |
| Wet film thickness | 55 – 70 μm |
| Theoretical spreading rate | 18.7 – 14 m²/l |
Drying and curing time
| Substrate temperature | 23 °C | 40 °C |
|---|---|---|
| Surface (touch) dry | 1 min | 20 sec |
| Walk-on-dry | 3 min | 1 min |