Marathon 500
Product Description
This is a two component polyamine cured epoxy coating. It is a surface tolerant, high solids, high build product. Will continue to cure when immersed in water. The product has high abrasion resistance. Suitable for environments with very high corrosivity, such as areas in the splash or tidal zone. Can be used as primer, mid coat, finish coat or as single coat system in atmospheric and immersed environments. Suitable for properly prepared carbon steel, galvanised steel, stainless steel, aluminium and concrete substrates.
Product data
Film thickness per coat
Drying and curing time
Product data
| Property | Test/Standard | Description |
|---|---|---|
| Solids by volume | ISO 3233 | 85 ± 2 % |
| Gloss level (GU 60 °) | ISO 2813 | gloss (70-85) |
Film thickness per coat
- Typical recommended specification range
| STANDARD GRADE | |
|---|---|
| Dry film thickness | 250 – 500 μm |
| Wet film thickness | 295 – 590 μm |
| Theoretical spreading rate | 3.4 – 1.7 m²/l |
Drying and curing time
| Substrate temperature | 10 °C | 15 °C | 23 °C | 40 °C |
|---|---|---|---|---|
| Surface (touch) dry | 14 h | 10 h | 4 h | 1.5 h |
| Walk-on-dry | 24 h | 18 h | 8 h | 3 h |